Effect of Glaze Cooling Rate on Mechanical Properties of Conventional and Pressed Porcelain on Zirconia

Abstract The aim of this study was to characterize a conventional and a pressed porcelain for zirconia core as to biaxial flexural strength (BFS), apparent fracture toughness (FT) and microstructure composition, and to investigate the effect of glaze cooling rate on the BFS of the zirconia/porcelain bilayers. Monolayers of conventional porcelain Vita VM9 and pressed porcelain Vita PM9 (n=15) (12 mm diameter x 1.2 mm thick) were prepared for the BFS test (MPa). Apparent fracture toughness (MPa.m1/2) was measured by indentation technique (n=15). t-Student test was performed for statistical analysis. Scanning electron microscopy and x-ray diffraction were used to analyze the porcelain's microstructure. For the BFS of bilayers, zirconia discs (12 mm diameter x 1 mm thick) (Vita In-Ceram YZ) were veneered with the two porcelains (1 mm thick). After the glaze firing simulation, the specimens were submitted to fast or slow cooling (n=15). Apparent fracture toughness (MPa.m1/2) was measured on the porcelain surface of bilayers (n=15) and residual stress was calculated. Two-way ANOVA (porcelain and cooling method) was used for the bilayer analysis (a=0.05). Vita PM9 monolayer exhibited significantly higher BFS (p<0.01), but there was no significant difference (p=0.41) in the FT between the porcelains. For bilayer specimens, the two-way ANOVA for BFS was significant for the porcelain variable only (p<0.01) better for Vita PM9/zirconia. Two-way ANOVA for the FT for the bilayers was not significant for any variable. All groups showed compressive residual stresses. The pressed porcelain seems to be mechanically more effective for zirconia veneering.

Resumo Este estudo teve como objetivo caracterizar uma porcelana convencional e uma prensada indicadas para infraestrutura de zircônia em termos de resistência à flexão biaxial (RFB), tenacidade à fratura aparente (TF) e composição microestrutural, e investigar o efeito da taxa de resfriamento do ciclo de glaze na RFB de espécimes bicamada de zircônia/porcelana. Espécimes monocamada de porcelana convencional Vita VM9 e porcelana prensada Vita PM9 (n=15) (12 mm de diâmetro x 1,2 mm de espessura) foram preparados para o ensaio de RFB (MPa). Tenacidade à fratura aparente (MPa.m1/2) foi mensurada pela técnica da indentação (n=15). O teste de t-Student foi aplicado para as análises estatísticas. Microscopia eletrônica de varredura e difração de raios-X foram utilizadas para análise microestrutural da porcelana. Para o ensaio de RFB nos bicamadas, discos de zircônia (12 mm de diâmetro x 1 mm de espessura) (Vita In-Ceram YZ) foram recobertos com as duas porcelanas (1 mm de espessura). Após a simulação da queima de glaze, os espécimes foram submetidos ao método de resfriamento rápido ou lento (n=15). A tenacidade à fratura aparente (MPa.m1/2) foi mensurado na superfície da porcelana dos bicamadas (n=15) e o estresse residual foi calculado. Foi utilizado ANOVA a dois fatores (porcelana e método de resfriamento) para análise estatística dos espécimes bicamada (a=0,05). Monocamadas de Vita PM9 exibiram valores de resistência à flexão biaxial significativamente maiores (p<0,01), mas não houve diferença estatística (p=0,41) em relação à TF entre as porcelanas. Para os espécimes bicamada, ANOVA a dois fatores para RFB foi significante apenas para a variável porcelana (p<0,01), com superioridade para Vita PM9/zircônia. ANOVA a dois fatores para TF dos espécimes bicamadas não apresentou significância para nenhuma variável. Todos os grupos apresentaram estresse residual de compressão. Porcelanas prensadas parecem ser mecanicamente mais efetivas para recobrimento de zircônia.

Comparison of the indentation strength and single-edge-v-notched beam methods for dental ceramic fracture toughness testing

Aim: To study influence of the cooling rate after sintering a veneering porcelain (Vita VM9) on fracture toughness by indentation strength (IS) and single-edge-v-notched beam (SEVNB) methods. Methods: Vita VM9 bars were sintered according to the manufacturer's recommendation and cooled under three conditions: Slow (inside the furnace from sintering temperature to room temperature); Normal (inside the furnace from sintering temperature to 500 ºC and outside the furnace from 500 ºC to room temperature); and Fast (outside the furnace from sintering temperature to room temperature). Fracture toughness was measured by IS (n=10) and SEVNB (n=10) methods. Data were analyzed by two-way ANOVA (α=0.05). Results: The fracture toughness obtained from SEVNB (slow - 1.02±0.10; normal - 1.09±0.13; and fast - 1,02±0.18 MPa.m1/2 cooling techniques) was significantly lower than IS (slow - 1.19±0.13; normal - 1.17±0.07; and fast - 1.16±0.06 MPa. m1/2 cooling techniques). There was no significant influence of the cooling technique (p=0.012). Conclusions: The measurement technique influenced the fracture toughness values . IS method overestimated the fracture toughness values. Irrespective of the measuring method, cooling rate did not influence the Vita VM9 veneering porcelain fracture toughness (Au)

Strength of 3Y-TZP and feldspathic porcelain subjected to different cooling methods

AIM: To investigate the effect of the cooling rate on flexural strength of monolayer and bilayer porcelain/zirconia (Y-TZP) bars. METHODS: Forty-five specimens were made for each design group: (PM) monolithic specimens of veneer porcelain Vita VM9 (Vita, Germany); (ZM) monolithic specimens of zirconia (ZiHP; ProtMat, Brazil); (PB) bilayer specimens zirconia/porcelain with porcelain on lower surface; and (ZB) bilayer specimens porcelain/zirconia with zirconia on lower surface. Each group was cooled by three different methods after porcelain sintering: slow specimens were cooled inside the turned-off furnace; normal specimens were removed from the furnace and cooled in air at room temperature; and fast specimens were removed from the furnace at 910°C and cooled by compressed air for 10 s. Specimens were polished and flexural strength was measured in water at 37 °C (n=15). Maximum load at fracture was recorded, and equations for simple (monolayer) and composite (bilayer) structures were used to calculate the flexural strength. RESULTS were analyzed using one-way ANOVA (p<0.05) and Tukey test separately for each design. RESULTS: The results of one-way ANOVA were statistically significant only for the PB group. The post-hoc Tukey test showed the highest flexural strength for fast cooling and the lowest for slow cooling; the normal cooling was statistically similar to both. CONCLUSIONS: Cooling methods affected only the flexural strength of bilayer specimens with porcelain on low surface (under tension) when the slow cooling method was used...

Effect of phosphate-bonded investments on titanium reaction layer and crown fit

This study analyzed the reaction layer and measured the marginal crown fit of cast titanium applied to different phosphate-bonded investments, prepared under the following conditions (liquid concentration/casting temperature): Rema Exakt (RE) - 100 percent/237°C, 75 percent/287°C, Castorit Super C (CS)-100 percent/70°C, 75 percent/141°C and Rematitan Plus (RP)- 100 percent/430°C (special to titanium cast, as the control group). The reaction layer was studied using the Vickers hardness test, and analyzed by two way ANOVA and Tukey's HSD tests (á = 0.05). Digital photographs were taken of the crowns seated on the die, the misfit was measured using an image analysis system and One-way ANOVA, and Tukey's test was applied (á = 0.05). The hardness decreased from the surface (601.17 VHN) to 150 ìm (204.03 VHN). The group CS 75 percent/141°C presented higher hardness than the other groups, revealing higher surface contamination, but there were no differences among the groups at measurements deeper than 150 ìm. The castings made with CS - 100 percent/70°C presented the lowest levels of marginal misfit, followed by RE -100 percent/237°C. The conventional investments CS (100 percent) and RE (100 percent) showed better marginal fit than RP, but the CS (75 percent) had higher surface contamination.

Protocolos clínicos atuais para os reimplantes dentais tardios / Actual clinical protocol to delayed dental replanation

Os casos de reimplante tardio de dentes avulsionados são considerados de prognóstico duvidoso, pois a ocorrência de anquilose e reabsorção são fatos comuns para esta condição. Com o intuito de prevenir tais conseqüências, a literatura propõe a utilização de substâncias no tratamento das superfícies radiculares dos dentes avulsionados cujo reimplante ocorra tardiamente. A proposta deste trabalho foi realizar uma discussão da literatura dentre as várias substâncias citadas e estudadas e apresentar protocolos de atendimento nas diversas situações possíveis. A remoção do ligamento periodontal e aplicação de solução de fluoreto de sódio a 2% por 20 minutos têm sido indicados no tratamento das superfícies radiculares de dentes reimplantados tardiamente. Além disso, muitos estudos estão sendo realizados com outras substâncias para tal finalidade, e algumas têm apresentado resultados promissores.

The delayed replantation of avulsed teeth has a critical long-term prognosis due to the common ankylosis and root resorpition ocurrency. The literature has purposed the use of several substances to the root surface treatment in order to delay or prevent these consequences. The aim of this study is to present a literature discussion about several substances studied, and discrible a clinical guidelines recommended to various situations. The periodontal ligament elimination and 2% sodium fluoride solution application for 20 minutes have been indicated to the root surface treatment in delayed tooth replantation. Furthermore, many studies have been done with other substances with the same goal and some of that have showed promising results.

Effect of surface treatments on the bond strength of a resin cement to commercially pure titanium

Investigation of the effectiveness of surface treatments that promote a strong bond strength of resin cements to metals can contribute significantly to the longevity of metal-ceramic restorations. This study evaluated the effect of surface treatments on the shear bond strength (SBS) of a resin cement to commercially pure titanium (CP Ti). Ninety cast CP Ti discs were divided into 3 groups (n=30), which received one of the following airborne-particle abrasion conditions: (1) 50 ?m Al2O3 particles; (2) 30 ?m silica-modified Al2O3 particles (Cojet Sand); (3) 110 ?m silica-modified Al2O3 particles (Rocatec). For each airborne-particle abrasion condition, the following post-airborne-particle abrasion treatments were used (n=10): (1) none; (2) adhesive Adper Single Bond 2; (3) silane RelyX Ceramic Primer. RelyX ARC resin cement was bonded to CP Ti surfaces. All specimens were thermally cycled before being tested in shear mode. Failure mode was determined. The best association was Rocatec plus silane. All groups showed 100 percent adhesive failure. There were combinations that promote higher SBS than the protocol recommended by the manufacturer of RelyX ARC.

A investigação da eficácia de tratamentos de superfície que promovem uma forte resistência de união de cimentos resinosos aos metais pode contribuir significantemente para a longevidade das restaurações metalocerâmicas. Este estudo avaliou o efeito de tratamentos de superfície na resistência ao cisalhamento da união de um cimento resinoso ao titânio comercialmente puro (Ti cp). Noventa discos foram fundidos em Ti cp e divididos em 3 grupos (n=30), os quais receberam uma das seguintes condições de jateamento: (1) partículas de Al2O3 de 50 ?m; (2) partículas de Al2O3 modificadas por sílica de 30 ?m (Cojet Sand); (3) partículas de Al2O3 modificadas por sílica de 110 ?m (Rocatec). Para cada condição de jateamento, os seguintes tratamentos pós-jateamento foram utilizados (n=10): (1) nenhum; (2) adesivo Adper Single Bond 2; (3) silano RelyX Ceramic Primer. O cimento resinoso RelyX ARC foi aplicado à superfície do Ti cp. Todos os espécimes foram termociclados antes do ensaio de cisalhamento. O modo de fratura também foi determinado. A melhor associação foi o Rocatec mais silano. Todos os grupos apresentaram 100 por cento de falha adesiva. Houve combinações que promoveram maior resistência ao cisalhamento da união que aquela recomendada pelo fabricante do RelyX ARC.

Influence of microwave sterilization on the cutting capacity of carbide burs

OBJECTIVE: This study compared the cutting capacity of carbide burs sterilized with microwaves and traditional sterilization methods. MATERIAL AND METHODS: Sixty burs were divided into 5 groups according to the sterilization methods: dry heat (G1), autoclave (G2), microwave irradiation (G3), glutaraldehyde (G4) or control - no sterilization (G5). The burs were used to cut glass plates in a cutting machine set for twelve 2.5-min periods and, after each period, they were sterilized (except G5) following the protocol established for each group. The cutting capacity of the burs was determined by a weight-loss method. Data were analyzed statistically by Kruskal-Wallis and Dunn's test. RESULTS: The means of the cutting amount performed by each group after the 12 periods were G1 = 0.2167 ± 0.0627 g; G2 = 0.2077 ± 0.0231 g; G3 = 0.1980 ± 0.0326 g; G4 = 0.1203 ± 0.0459 g; G5 = 0.2642 ± 0.0359 g. There were statistically significant differences among the groups (p<0.05); only dry heat sterilization was similar to the control. CONCLUSION: Sterilization by dry heat was the method that least affected the cutting capacity of the carbide burs and microwave sterilization was not better than traditional sterilization methods.

Reparo intraoral de próteses metalo-cerâmicas : um relato de caso clínico / Intraoral repair in metal-ceramic prostheses: a clinical report

Repairing fractured metal-ceramic prosthesis is a treatment alternative that can increase the restoration longevity, preserve dental structure, and/or the integrity of implant components, besides being a simple, low-cost technique. However, clinicians often see restoration repair as a challenge because of the many doubts regarding the procedures required to obtain satisfactory results. Therefore, the motivation to write this article is the need to provide instructions for clinicians dealing with a situation involving fractured porcelain, presenting an intraoral repair technique that can be used in cases of a fractured ceramic veneer of a fixed partial prosthesis. The technique consisted in treating the remaining ceramic surface and applying a microhybrid composite resin following the steps of a protocol that, according to scientific evidence, has promoted high bond strength to porcelain, in addition to being cost effective.

O reparo de próteses metaloceramicas, quando a cerâmica encontra-se fraturada, e um tratamento alternativo que pode aumentar a longevidade dessas restaurações, preservar a estrutura dental ou a integridade de componentes protéticos sobre implantes, alem de ser uma técnica simples e de baixo custo. No entanto, essa técnica, geralmente, e vista como um desafio pelos cirurgiões-dentistas uma vez que não ha um protocolo clinico bem estabelecido para a obtenção de resultados satisfatórios. Assim sendo, o objetivo deste artigo e prover instruções para os clínicos lidarem com situações de fratura da cerâmica por meio da apresentação de um caso clinico, no qual uma técnica de reparo intra-oral indicada para essa situação foi empregada. Essa técnica consiste em tratar a superfície da cerâmica remanescente e aplicar uma resina composta microhibrida, seguindo os passos de um protocolo que, de acordo com evidencias cientificas, tem promovido alta resistência de união, alem de apresentar um baixo custo.

Internal adaptation of cast titanium crowns

As the adaptation of titanium crowns obtained by Rematitan Plus investment, specific for titanium, is not recognized to be suitable, this study evaluated the effect of the concentration of the specific liquid and the temperature of the mold of investments on the internal misfit of crowns cast on commercially pure titanium. Individual dies of epoxy resin were obtained, representing teeth prepared for full-crown restoration with a 6-degree axial surface convergence angle and shoulder (1.0 mm). For the waxing of each crown, a ring-shaped stainless steel matrix (8.0mm internal diameter; 7.5 mm height) was adapted above the individual dies of epoxy resin. The Rematian Plus investment was mixed according to the manufacturer's instructions using two different concentrations of the specific liquid: 100 percent, 75 percent. Casting was performed in a Discovery Plasma Ar-arc vacuum-pressure casting machine with molds at temperatures of 430°C, 515°C and 600°C. The crowns were cleaned individually in a solution (1 percent HF + 13 percent HNO3) for 10 min using a ultrasonic cleaner, with no internal adaptations, and luted with zinc phosphate cement under a 5 kg static load. The crown and die assemblies were embedded in resin and sectioned longitudinally. The area occupied by cement was observed using stereoscopic lens (10X) and measured by the Leica Qwin image analysis system (mm²). The data for each experimental condition (n=8) were analyzed by Kruskal-Wallis non-parametric test (á=0.05). The results showed that liquid dilution and the increase in mold temperature did not significantly influence the levels of internal fit of the cast titanium crowns. The lowest means (±SD) of internal misfit were obtained for the 430°C/100 percent: (7.25 mm² ±1.59) and 600°C/100 percent (8.8 mm² ±2.25) groups, which presented statistically similar levels of internal misfit.

Influence of the final temperature of investment healting on the tensile strength and Vickers hardness of CP Ti and Ti-6Al-4V alloy

The aim of the work was to evaluate the influence of the temperature of investment healting on the tensile strength and Vickers hardness of CP Ti and Ti-6Al-4V alloy casting. Were obtained for the tensile strength test dumbbell rods that were invested in the Rematitan Plus investment and casting in the Discovery machine cast. Thirty specimens were obtained, fiftten to the CP Titanium and fifteen to the Ti-6Al-4V alloy, five samples to each an of the three temperatures of investment: 430°C (control group), 480°C and 530°C. The tensile test was measured by means of a universal testing machine, MTS model 810, at a strain of 1.0 mm/min. After the tensile strenght test the specimens were secctioned, embedded and polished to hardness measurements, using a Vickers tester, Micromet 2100. The means values to tensile tests to the temperatures 430°C, 480 and 530: CP Ti (486.1 - 501.16 - 498.14 -mean 495.30 MPa) and Ti-6Al-4V alloy (961.33 - 958.26 - 1005.80 - mean 975.13 MPa) while for the Vickers hardness the values were (198.06, 197.85, 202.58 - mean 199.50) and (352.95, 339.36, 344.76 - mean 345.69), respectively. The values were submitted to Analysis of Variance (ANOVA) and Tukey,s Test that indicate differences significant only between the materials, but not between the temperature, for both the materias. It was conclued that increase of the temperature of investment its not chance the tensile strength and the Vickers hardness of the CP Titanium and Ti-6Al-4V alloy.

Estudo in vitro da infiltração marginal em cavidades classe V restauradas com resinas compostas posteriores / In vitro study of marginal leakage in cavities class V restorations posterior composite

A proposta deste estudo foi verificar a infiltração marginal de cavidades classe V utilizando resinas compostas posteriores. Foram preparados na face vestibular de 30 incisivos bovinos, preparos cavitários classe padronizada com término em esmalte. Em seguida, os dentes foram divididos em três grupos e restaurados utilizando os materiais de acordo com as instruções dos fabricantes, ou seja: Grupo I: Etch&Prime 3.0 (Degussa) + Definite (Degussa); Grupo II: Admira Bond (Voco) + Prodigy Condensable (Kerr) e Grupo III: Admira Bond (Voco) + Admira (Voco). Após restaurados, os dentes foram submetidos a 500 ciclos térmicos e isolados com esmalte para unha. Após, foram imersos em solução de azul de metileno a 2% tamponado, por 2 horas. Em seguida, foram seccionadas e analisadas em lupa estereoscópica para qualificar os níveis de infiltração. Os resultados foram analisados estatisticamente pelo teste Kruskal Wallis. Observou-se escore médio de 1,45 para o Grupo III, apresentando estatisticamente menor infiltração marginal, seguido do Grupo II (2,70) e posteriormente Grupo I (3,45), os quais diferiram entre si. O sistema restaurador Admira Bond + Admira apresentou menor infiltração diante dos demais sistemas restauradores

Flexural strength of direct composites submitted to post-polymerization heat

O objetivo deste estudo foi avaliar os efeitos da polimerização térmica adicional na resistência à flexão de compósitos diretos. Os espécimes dos compósitos diretos (Z250 e P60) (n=10), medindo 25×2×2 mm, foram polimerizados por três métodos: (1) fotopolimerização por 40 segundos, (2) (1) + polimerização adicional em estufa a 120°C por 20 minutos, e (3) (1) + polimerização adicional em autoclave a 120°C por 20 minutos. Os espécimes (n=10) do compósito indireto Artglass (grupo controle) foram polimerizados no forno UniXS. Os espécimes foram armazenados em água destilada por 24 horas a 37°C e então submetidos ao teste de resistência à flexão. Os dados de resistência à flexão foram analisados por análise de variância e teste Tukey (α=0,05). Os resultados mostraram que (1) a polimerização térmica adicional em estufa resultou em resistência à flexão significativamente maior (p<0,05) (Z250: 158,85 MPa e P60: 147,10 MPa) que a resina Artglass (121,52 MPa); (2) com a polimerização em autoclave, os compósitos diretos apresentaram médias de resistência à flexão (Z250: 134,54 MPa e P60: 130,18 MPa) similares à resina Artglass (p>0,05); (3) os grupos apenas fotopolimerizados (Z250: 124,75 MPa e P60: 128,96 MPa) foram similares à resina Artglass (p>0,05). Quando os compósitos foram apenas fotopolimerizados, eles mostraram comportamento de resistência à flexão similar ao compósito indireto Artglass.

Resistência à compressão de revestimentos fosfatados para fundição de titânio em diferentes remperaturas / Compressive strength of phosphate investment for casting of the titanium on different temperatures

O titânio apresenta características favoráveis que o torna uma excelente alternativa ao uso de ligas áureas, porém seu elevado ponto de fusão e a baixa densidade exigem máquinas especiais de fundição e revestimento resistente para suportar o processo. Esse estudo avaliou a resistência à compressão de três revestimentos fosfatados, sendo um deles específico para titânio Rematitan Plus (RP) e dois alternativos, Rema Exakt (RE) e Castorit Super C (CA), variando-se a temperatura final do ciclo (600, 515 e 430 °C). Para o ensaio de resistência à compressão, os corpos-de-prova cilíndricos (n = 10) com 20 mm de diâmetro e 40 mm de altura foram obtidos em uma matriz metálica bipartida. Após 12 horas, foram submetidos à queima em forno (EDG) conforme instruções do fabricante. Ao atingir a temperatura final programada, foi realizado o teste, em máquina de ensaios mecânicos MTS 810, à velocidade de 2 mm.min-1 até a fratura do corpo-de-prova. Após os testes, os valores de resistência em MPa foram analisados por meio do software SPSS 11.0. Aplicou – se análise de variância e teste de Tukey para comparação dos grupos (P = 0,05). Em cada temperatura, o RE apresentou maior resistência que o RP, que, por sua vez, foi superior ao CA. Analisou-se, também, a influência das temperaturas para cada material. Em geral, os materiais na temperatura final de 600 °C foram mais resistentes do que em 515 e 430 °C, que mostraram comportamento variável. Concluiu-se que o revestimento alternativo RE apresentou resistência à compressão superior à do específico para titânio e que a variação na temperatura final influenciou diferentemente cada material.

The titanium has favorable characteristics that become an excellent alternative to the use of golden alloys. However, his high point of fusion and the low density require special machines of castingand resistant dental investments for this process.This study evaluated the strength to the compression of three phosphate-bonded investments, one of them specific for titanium - Rematitan Plus (RP), and two alternative Rema Exakt (RE) and Castorit Super C (CA), in different end temperatures of the cycle (600, 515 and 430 °C). For the strength to the compression, cylindrical specimens with 20 mm of diameter and 40 mm of height were obtained in a bipartite metallic matrix (n = 10), after 12 hours were submitted to the burns in oven (EDG), in according to the instructions of the manufacturer. Upon reaching the end programmed temperature, was done the test in machine of mechanical test MTS 810 (MTS System Corporation, Minnesota, EUA), in speed of 2mm.min_1 up to fracture of the specimens. After the tests the values of resistance in MPa were analyzed utilizing the software SPSS 11.0. It applied – itself ANOVA and test of Tukey for comparison of the groups (P = 0.05) and compared the material in each temperature, the RE presented bigger resistance than to of the RP, that by his time was a superior to of the CA. Analyzed itself the influence of the temperatures for each material. The materials in the end temperature of 600 °C were more resistant than in 515 and 430 °C. It was possible to conclude that the dental investments RE showed highest strength than the specific investment and the final temperature influenced differently this property of the materials.

Estudo do conteúdo de partícula inorgânica de resinas compostas diretas e indiretas / Study of the direct and indirect composite resin's inorganic contents

O propósito deste estudo foi avaliar o conteúdo de partícula inorgânica em massa e volume de resinas compostas de aplicação direta e indireta. Para a avaliação das partículas inorgânicas foram confeccionados cinco corpos-de-prova cilíndricos, com 5x2mm para cada material. Foram ativados por 40 segundos e pesados em balança analítica (Sartorius) à seco e imersos em água destilada. Após a eliminação da matriz orgânica realizada em forno elétrico a 700ºC por 3 horas, foram pesados à seco e armazenados em água destilada, por 7 dias para nova pesagem em imersão. O conteúdo por massa foi baseado na aplicação do Princípio de Arquimedes...

Vickers hardness of cast commercially pure titanium and Ti-6Al-4V alloy submitted to heat treatments

O objetivo deste estudo foi avaliar o efeito de tratamentos térmicos na dureza Vickers do titânio comercialmente puro e da liga Ti-6Al-4V. Corpos-de-prova cilíndricos com 6 mm de diâmetro foram fundidos no sistema Rematitan. Os corpos-de-prova de titânio comercialmente puro e da liga Ti-6Al-4V foram divididos aleatoriamente em 3 grupos (n=10): controle (sem tratamento térmico); tratamento 1 (T1): aquecido a 750ºC por 2 h; tratamento 2 (T2): aquecido a 955ºC por 1 h e envelhecido a 620ºC por 2 h. Após os tratamentos térmicos, os corpos-de-prova foram incluídos em resina acrílica, a superfície foi regularizada e polida, e a dureza foi mensurada. As médias de dureza Vickers (VHN) e os desvios padrão foram analisados estatisticamente usando o teste de Kruskal-Wallis com nível de significância a 5%. Para o titânio comercialmente puro, a média de dureza do grupo T2 (259,90 VHN) foi significativamente maior que os outros grupos (controle-200,26 VHN e T1-202,23 VHN) (p<0,05), que apresentaram valores médios similares (p>0,05). Para a liga Ti-6Al-4V, diferenças estatisticamente significantes foram observadas entre os três grupos: T2 (369,08 VHN), T1 (351,94 VHN) e controle (340,51 VHN) (p<0,05). Os resultados demonstraram diferente comportamento de dureza do titânio comercialmente puro e da liga Ti-6Al-4V quando diferentes tratamentos foram usados. Para o titânio comercialmente puro, a média de VHN grupo T2 foi consideravelmente maior que as médias dos grupos controle e T1, os quais demonstraram médias similares entre si. Para a liga Ti-6Al-4V, entretanto, a média de VHN registrada para cada grupo pode ser apresentada da seguinte maneira: T2>T1>controle.

Influence of activation modes on diametral tensile strength of dual-curing resin cements

Em restaurações metálicas, a polimerização dos cimentos resinosos duais depende exclusivamente da ativação química. Há poucas pesquisas sobre o efeito da supressão da fotoativação na resistência desses cimentos. Este estudo avaliou a influência de métodos de ativação na resistência à tração diametral (RTD) de cimentos resinosos duais. Pastas base e catalisadora do Panavia F, Variolink II, Scotchbond Resin Cement, Rely X e Enforce foram espatuladas e inseridas em matrizes metálicas cilíndricas (4 x 2 mm). Os cimentos foram: 1) não fotoativados (ativação química = grupos quimicamente ativados) ou 2) fotoativados através de tira de poliéster (ativação química e foto = grupos duais) (n = 10). Após armazenamento por 24 horas em água destilada a 37ºC, os espécimes foram submetidos a forças de compressão. Um cimento resinoso de ativação química (Cement-It) e um de fosfato de zinco serviram como grupos controle. Foram feitas as seguintes comparações: 1) entre os métodos de ativação (grupos quimicamente ativados e grupos duais), para cada cimento resinoso dual, por meio do testet de Student; 2) entre os grupos quimicamente ativados dos cimentos resinosos duais e os grupos controle, empregando-se ANOVA e teste de Tukey (a = 0,05). Os grupos duais do Scotchbond Resin Cement (53,3 MPa), Variolink II (48,4 MPa) e Rely X (51,6 MPa) tiveram maior RTD do que os seus grupos quimicamente ativados (44,6; 40,4 e 44,5 MPa, respectivamente) (p < 0,05). Para o Enforce (48,5 e 47,8 MPa) e para o Panavia F (44,0 e 43,3 MPa), não houve diferença significativa entre os métodos de ativação (p > 0,05). Os grupos quimicamente ativados dos cimentos duais apresentaram RTD estatisticamente semelhante à do Cement-It (44,1 MPa) (p > 0,05), e maior que a do fosfato de zinco (4,2 MPa). Scotchbond Resin Cement, Variolink II e Rely X dependeram da fotoativação para alcançar valores máximos de RTD. Na ausência de luz, todos os cimentos duais apresentaram maior RTD que a do fosfato de zinco, e RTD estatisticamente semelhante à do Cement-It (p > 0,05).

Compressive strength and compressive fatigue limit of conventional and high viscosity posterior resin composites

O objetivo deste estudo foi comparar a resistência à compressão e o limite de fadiga compressiva de três resinas compostas indicadas para dentes posteriores (Filtek P-60, Surefil e Prodigy Condensable) e uma universal (Z-100). Corpos-de-prova cilíndricos (8 mm de altura x 4 mm de diâmetro) foram usados. O teste dinâmico foi realizado usando-se o método escada e a relação entre limite de fadiga compressiva, e resistência à compressão também foi calculada (n = 15). Os dados de resistência à compressão e de limite de fadiga compressiva foram submetidos à Anova e ao teste de Tukey. O compósito Z-100 apresentou maior resistência à compressão (307,20 MPa) que Surefil (266,93 MPa) e Prodigy Condensable (222,08 MPa). A resistência de Filtek P-60 (270,44 MPa) foi similar à de Z-100 e à de Surefil, enquanto Prodigy Condensable apresentou a menor resistência à compressão. No teste de limite de fadiga compressiva, Filtek P-60 mostrou maior valor (184,20 MPa) que Prodigy Condensable (155,50 MPa). Os compósitos Surefil (165,74 MPa) e Z-100 (161,22 MPa) mostraram-se similares a Filtek P-60 e Prodigy Condensable. A relação limite de fadiga compressiva/resistência à compressão foi de 70,01% para Prodigy Condensable, 68,11% para Filtek P-60, 62,09% para Surefil e 52,48% para Z-100. Foi concluído que o compósito universal Z-100 foi mais sensível ao teste dinâmico que os materiais de alta viscosidade.

Polimerização de resina composta com interposição de esmalte, dentina ou resina incisal / Polymeration of composite resin with interposition of enamel, dentin or incisal resin

Esse estudo avaliou, por meio de ensaios de dureza, a profundidade de polimerização de uma resina composta (TPH), após a interposição de camadas de esmalte, dentina ou resina incisal. As medidas de dureza foram efetuadas no primeiro e no segundo milímetro abaixo da superfície do compósito. De acordo com os resultados, os valores de dureza diminuíram com o aumento da profundidade e da espessura da camada interposta. Entretanto, para uma mesma espessura não houve diferença significativa para os valores de dureza, independentemente do material interposto

The influence of chemical activation on hardness of dual-curing resin cements

Na cimentação de restaurações metálicas, a polimerização dos cimentos resinosos duais depende exclusivamente da ativação química. Este estudo avaliou a influência da ativação química, comparada à dupla ativação (química e pela luz), na dureza de 4 cimentos resinosos duais. Em ambiente isento de luz, quantidades iguais em massa das pastas base e catalisadora dos cimentos Scotchbond Resin Cement, Variolink II, Enforce e Panavia F foram espatuladas e inseridas em matrizes com cavidade de 4 mm de diâmetro e 2 mm de altura. A seguir, os cimentos foram: 1) mantidos no escuro (ativação química = grupos quimicamente ativados) ou 2) fotopolimerizados (dupla ativação = grupos duais). A dureza Vickers foi obtida 1 hora, 24 horas e 7 dias após o início da espatulação dos cimentos. Em todos os cimentos, a dureza dos grupos quimicamente ativados foi menor que a dos respectivos grupos duais nos tempos de 1 hora e de 24 horas. Aos 7 dias, esse comportamento foi mantido pelo Variolink II e Panavia F, enquanto para o Scotchbond Resin Cement e para o Enforce não houve diferença estatisticamente significante entre os dois métodos de ativação. Todos os cimentos mostraram aumento significativo de dureza de 1 hora para 7 dias, em ambos os métodos de ativação. Dentre os grupos quimicamente ativados, o Scotchbond Resin Cement e o Variolink II mostraram, respectivamente, a maior e a menor dureza nos três tempos testados. Dentro dos limites deste estudo, até o período de 24 horas, a ativação exclusivamente química não foi capaz de promover dureza semelhante à obtida pela dupla ativação.

Tratamento de superfície de restaurações estéticas indiretas para cimentação adesiva / Surface treatment of indirect esthetic restorations

O objetivo deste trabalho foi o de realizar uma revisão de literatura a respeito dos tratamentos de superfície existentes para a cimentação adesiva de peças protéticas confeccionadas em cerâmica ou resina composta, no que diz respeito à resistência de união. Com base na literatura consultada, foi possível concluir que existam poucos trabalhos que indiquem o melhor tratamento para restaurações em resina composta indireta. Em relação às restaurações cerâmicas com alto conteúdo de sílica, o tratamento com jateamento ou ácido fosfórico, seguido da aplicação de silano, tem demonstrado bons resultados. Nos sistemas In-Ceram e Procera All-Ceram, estariam indicados o jateamento e o sistema de sinalização Rocatec. Os cimentos resinosos que contém MDP, como o Panavia, seriam os mais indicados